Phase formation,microstructure development,and mechanical properties of kaolin-based mullite ceramics added with Fe2O3

The effects of Fe₂O₃ on phase evolution, density, microstructural development, and mechanical properties of mullite ceramics from kaolin and alumina were systematically studied. X-ray diffraction results suggested that the ceramics consisted of mullite, sillimanite, and corundum, in the sintering range of 1450°C–1580°C. However, as the sintering was raised to 1580°C, mullite is the main phase with a content of 94%, and the corundum phase content is 5.9%. Simultaneously, high-temperature sintering had a positive effect on the densification of the mullite ceramics, where both the bulk density and flexural strength could be optimized by adjusting the content of Fe₂O₃. It was found that 6 wt% Fe₂O₃ was optimal for the formation of rod-shaped mullite after sintering at 1550°C for 3 h. The sample's maximum bulk density was 2.84 g/cm³, with a flexural strength of 112 MPa. Meanwhile, rod-shaped mullite grains with an aspect ratio of ~9 were formed. As a result, a dense network structure was developed, thus leading to mullite ceramics with excellent mechanical properties. The effect of Fe₂O₃ on the properties might be attributed to the fact that Al³⁺ ions in the [AlO₆] octahedron were replaced by Fe³⁺ ions, resulting in lattice distortion.