Thermal Conductivity and Interfacial Thermal Resistance: Measurements of Thermally Oxidized SiO2 Films on a Silicon Wafer Using a Thermo-Reflectance Technique

This article describes the development of a method to measure the normal-to-plane thermal conductivity of a very thin electrically insulating film on a substrate. In this method, a metal film, which is deposited on the thin insulating films, is Joule heated periodically, and the ac-temperature response at the center of the metal film surface is measured by a thermo-reflectance technique. The one-dimensional thermal conduction equation of the metal/film/substrate system was solved analytically, and a simple approximate equation was derived. The thermal conductivities of the thermally oxidized SiO₂ films obtained in this study agreed with those of VAMAS TWA23 within ± 4%. In this study, an attempt was made to estimate the interfacial thermal resistance between the thermally oxidized SiO₂ film and the silicon wafer. The difference between the apparent thermal resistances of the thermally oxidized SiO₂ film with the gold film deposited by two different methods was examined. It was concluded that rf-sputtering produces a significant thermal resistance ((20 ± 4.5) × 10⁻⁹ m²·K·W⁻¹) between the gold film and the thermally oxidized SiO₂ film, but evaporation provides no significant interfacial thermal resistance (less than ± 4.5 × 10⁻⁹ m²·K·W⁻¹). The apparent interfacial thermal resistances between the thermally oxidized SiO₂ film and the silicon wafer were found to scatter significantly (± 9 × 10⁻⁹ m²·K·W⁻¹) around a very small thermal resistance (less than ± 4.5 × 10⁻⁹ m²·K·W⁻¹).