Hot-Pressing of Si3N4 with Y2O3 and Li2O as Additives

The rates of densification and phase transformation undergone by α-Si₃N₄ during hot-pressing in the presence of Y₂O₃, Y₂O₃−2SiO₂, and Li₂0−2Si0₂ as additives were studied. Although these systems behave less simply than MgO-doped Si₃N₄, the data can be interpreted during the early stages of hot-pressing as resulting from a solution-diffusion-reprecipitation mechanism, where the diffusion step is rate controlling and where the reprecipitation step invariably results in the formation of the β-Si₃N₄ phase.