| 稀土处理钢保护渣的研究与应用 |
| |
| 引用本文： | 万恩同. 稀土处理钢保护渣的研究与应用[J]. 稀土, 2001, 22(4): 72-75 |
| |
| 作者姓名： | 万恩同 |
| |
| 作者单位： | 武钢技术中心, |
| |
| 摘 要： | 减少保护渣中的Na2O、SiO2而增加Al2O3,以减少RExOy的产生;增加B2O3组元作助熔剂,并且提高溶解RExOy的能力.试验结果表明,浇铸09CuPTiRE钢保护渣使用状况良好,铸坯表面无纵裂纹等缺陷,没有发生漏钢事故;熔渣中RExOy含量3.4%,99%为玻璃相.
|
| 关 键 词： | 稀土处理钢 保护渣 RExOy 玻璃相 晶相 |
| 文章编号： | 1004-0277(2001)04-0072-04 |
| 修稿时间： | 2001-06-05 |
Research and Application of Mold Flux for Steels Treated with Rare Earth |
| |
| WAN En tong. Research and Application of Mold Flux for Steels Treated with Rare Earth[J]. Chinese Rare Earths, 2001, 22(4): 72-75 |
| |
| Authors: | WAN En tong |
| |
| Abstract: | With the Na 2O% and SiO 2% decreasing and Al 2O 3% increasing,the generation of RE xO y in molten flux can be reduced.The ability of RE xO y dissolving can be improved by adding B 2O 3 composite as solvent.A plant trial with improved flux was carried out.It has contributed good performance and surface quality,sticking break was free.Compared with 6.3% RE xO y content and 97% crystallization in molten flux tested using other flux,RE xO y content and glass phase were 3.8% and 99% respectively. |
| |
| Keywords: | mold flux RE xO y glass phase crystallization |