Fabrication and mechanical properties of short ZrO2 fiber reinforced NiFe2O4 matrix composites

Short ZrO₂ fibers (ZrO_2(f)) reinforced NiFe₂O₄ ceramic composites were fabricated by cold pressing process. The phase composition, microstructure, mechanical properties and fiber/matrix interface of the composites were investigated by X-ray diffraction, scanning electron microscopy and mechanical testing machines. ZrO_2(f) show good thermodynamic and chemical compatibility with NiFe₂O₄ ceramic matrix and effectively enhanced the mechanical properties. The toughening mechanisms are fiber bridging, interfacial debonding, fiber pullout, phase transformation and the matrix constraint effect. By incorporation of 3 wt% fibers with the average length of 5～6 mm, the bending strength and fracture toughness of the composites reached 88.92 MPa and 4.62 MPa m^1/2, respectively, while the strength conservation ratio after thermal shock increased from 48.85% to 75.86%. The weak interface bonding built up between ZrO_2(f) and NiFe₂O₄ facilitates the reinforcing effects of the fibers to operate.