Influence of niobium doping on phase composition and defect-mediated photoluminescence properties of Eu-doped TiO2 nanopowders synthesized in Ar/O2 thermal plasma

Nb⁵⁺:Eu³⁺-codoped TiO₂ nanopowders for chemical composition adjustment have been synthesized via Ar/O₂ radio-frequency thermal plasma. X-ray diffraction (XRD) results reveal that all the resultant powders exhibited mixture polymorphs of anatase (mean size: ∼45 nm) as the major phase and rutile (mean size: ∼71 nm). Rutile formation was promoted by the Eu³⁺ doping but suppressed by the Nb⁵⁺ addition. Combined observation using FE-SEM and TEM indicates that all the plasma-synthesized powders had a majority of facet-shaped particles (several nanometers) and a small proportion of nearly spherical crystals (∼150 nm). For the defect-mediated photoluminescence (PL) emission through the energy transfer from the TiO₂ host to the Eu³⁺ activator, the PL intensity originating from the ⁵D₀ → ⁷F₂ electronic transition weakened but that from the ⁵D₀ → ⁷F₁ electronic transition strengthened with increasing Nb⁵⁺ content. This may be a result of the decrease in the oxygen vacancy defects in the TiO₂ host lattice, as revealed by the joint means of UV-vis absorption spectra and excitation and emission spectra.