| 表面高铬高碳合金层的研究 |
| |
| 引用本文： | 高原,芦金斌,徐重.表面高铬高碳合金层的研究[J].化工机械,2003,30(3):143-146,151. |
| |
| 作者姓名： | 高原 芦金斌 徐重 |
| |
| 作者单位： | 太原理工大学 |
| |
| 摘 要： | 采用双层辉光等离子表面合金化方法 ,在A3钢表面形成高铬高碳表面合金化层。合金层中的碳化物细小、弥散、均匀 ,且不含粗大共晶莱氏体组织 ,硬度高 ,耐磨性好。与GCr15淬火钢相比 ,耐磨性提高 8.6倍
|
| 关 键 词： | 渗铬 等离子 碳化物 渗碳 |
| 文章编号： | 0254-6094(2003)03-0143-05 |
Research on the Surface With High Chromium and High Carbon Alloy Layer |
| |
| GAO Yuan,LU Jinbin,XU Zhong.Research on the Surface With High Chromium and High Carbon Alloy Layer[J].Chemical Engineering & Machinery,2003,30(3):143-146,151. |
| |
| Authors: | GAO Yuan LU Jinbin XU Zhong |
| |
| Abstract: | A high chromium and high carbon surface alloy layer was formed on A3 steel surface using the double glow plasma surface alloy method. The carbide in the alloy layer was fine, dispersive, uniform, hard, wear resistant, and had not coarse ledeburite structure. In comparison with GCr15 quenched steel, the wear resistance of the alloy layer was higher than a 8.6 fold increase. |
| |
| Keywords: | Chromium Impregnation Plasma Carbide Carburization |