| 加压碳化法制备微纳米棒状碳酸钙 |
| |
| 引用本文： | 王爽,燕溪溪,苏晴,黎晨欣,申韬艺,肖容慧,王利军. 加压碳化法制备微纳米棒状碳酸钙[J]. 上海第二工业大学学报, 2021, 38(2): 123-130 |
| |
| 作者姓名： | 王爽 燕溪溪 苏晴 黎晨欣 申韬艺 肖容慧 王利军 |
| |
| 作者单位： | 上海第二工业大学 环境与材料工程学院,上海201209;上海第二工业大学 环境与材料工程学院,上海201209;宁波聚才新材料科技有限公司,浙江宁波315311;复旦大学 聚合物分子工程国家重点实验室,上海200433 |
| |
| 基金项目： | 宁波市 3315 资本引才计划 (2020C-04-T) 资助 |
| |
| 摘 要： | 以六偏磷酸钠作为晶型控制剂,在碳化法的基础上采用加压的方式制备出分散度较好、粒径可达到微纳米级别的碳酸钙,形貌呈明显的棒状.研究了反应温度、反应时间、六偏磷酸钠的添加量、氢氧化钙的浓度等实验条件对制备碳酸钙样品的影响,得出制备的最佳条件.分别利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、粒度分析仪等测试方式对合...
|
| 关 键 词： | 加压碳化 六偏磷酸钠 微纳米技术 棒状碳酸钙 |
Preparation of Micro-Nano Rod-Shaped Calcium Carbonate by Pressurized Carbonization Method |
| |
| WANG Shuang,YAN Xi-xi,SU Qing,LI Chen-xin,SHEN Tao-yi,XIAO Rong-hui and WANG Li-jun. Preparation of Micro-Nano Rod-Shaped Calcium Carbonate by Pressurized Carbonization Method[J]. Journal of Shanghai Second Polytechnic University, 2021, 38(2): 123-130 |
| |
| Authors: | WANG Shuang YAN Xi-xi SU Qing LI Chen-xin SHEN Tao-yi XIAO Rong-hui WANG Li-jun |
| |
| Affiliation: | 1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China;,1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China;,1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China;,1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China;,1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China;,1. School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China; and 2. Ningbo Jucai New Material Technology Co., Ltd, Ningbo 315311, Zhejiang, China; 3. State Key Laboratory ofMolecular Engineering of Polymers, Fudan University, Shanghai 200433, China |
| |
| Abstract: | |
| |
| Keywords: | high-pressure carbonization sodium hexametaphosphate micro-nano technology rod-shaped calcium carbonate |