Fabrication of Nano-Scaled α-Al2O3 Crystallites Through Heterogeneous Precipitation of Boehmite in a Well-Dispersed θ-Al2O3-Suspension

The possibility of eliminating finger or vermicular growth of α-Al₂O₃ particles obtained by calcination of boehmite was examined. Heterogeneous precipitation of boehmite in a well-dispersed θ-Al₂O₃ suspension was first prepared, in which the mass ratio of boehmite to θ-crystallite was evaluated to form agglomerates of similar sizes that will form α-Al₂O₃ crystallites of <100 nm in diameter. θ- to α-phase transformation of alumina experiences a nucleation and growth mechanism, with the critical size of nucleation being ～25 nm for θ-Al₂O₃ and the size for accomplishment of transformation followed by finger growth being ～100 nm. Hence, fabricating agglomerates that would form α-Al₂O₃ crystallites with sizes <100 nm accompanied with appropriate thermal treatments can be a method for obtaining α-Al₂O₃ crystallites free of finger growth. It is found that proper preparation of the agglomerate with appropriate size may initiate a simultaneous and lower temperature θ- to α-Al₂O₃ phase transformation for such powder systems, substantially limiting the mass transfer among the newly formed α-Al₂O₃ particles. Moreover, α-Al₂O₃ crystallites free of finger growth can be obtained.