| 耐候钢连铸坯表面纵裂原因分析 |
| |
| 引用本文： | 韩振东,辛建卿,李建民.耐候钢连铸坯表面纵裂原因分析[J].山西冶金,2006,29(2):69-70. |
| |
| 作者姓名： | 韩振东 辛建卿 李建民 |
| |
| 作者单位： | 太原钢铁(集团)有限公司,山西,太原,030003 |
| |
| 摘 要： | 结合实际生产情况，分析了耐候钢连铸坯表面纵裂纹成因，提出了控制该缺陷的工艺措施，介绍了所取得的效果。
|
| 关 键 词： | 耐候钢 纵裂 原因 |
| 文章编号： | 1672-1152(2006)02-0069-02 |
| 收稿时间： | 04 25 2006 12:00AM |
| 修稿时间： | 2006年4月25日 |
Causes of Longitudinal Crack on the Continuously Casting Slabs of Atmosphere Corrosion Resisting Steel |
| |
| HAN Zhendong,XIN Jianqing,Li Jianming.Causes of Longitudinal Crack on the Continuously Casting Slabs of Atmosphere Corrosion Resisting Steel[J].Shanxi Metallurgy,2006,29(2):69-70. |
| |
| Authors: | HAN Zhendong XIN Jianqing Li Jianming |
| |
| Abstract: | Causes of longitudinal crack on the continuously casting slab of atmosphere corrosion resisting steel are analyzed, the measures of controlling the defect are presented, and the results which have been obtained are introduced. |
| |
| Keywords: | atmosphere corrosion resisting steel longitudinal crack cause |