Microstructural changes during ageing of Cu-2.5 wt% Ti |
| |
Authors: | P E Donovan A W Thompson |
| |
Affiliation: | (1) Department of Materials Science and Metallurgy, University of Cambridge, Pembroke Street, Cambridge, UK;(2) Department of Metallurgical Engineering and Materials Science, Carnegie-Mellon University, Pittsburgh, PA, USA |
| |
Abstract: | Microstructural changes in Cu-2.5wt % Ti during ageing at 573 and 773 K have been studied by transmission electron microscopy. Ageing times ranged from 60 sec to 200 h. Ordering of the![beta](/content/u1350r538276084g/xxlarge946.gif) precipitates was observed after very short ageing treatments at 773 K, and coarsening according tot
1/3 was also observed from very early times. The![beta](/content/u1350r538276084g/xxlarge946.gif) particles were observed to become increasingly aligned into rod-like groups along 10 0 as ageing progressed. These results permit a new interpretation of the strengthening mechanisms in this alloy. |
| |