| 冷拔后退火对Monel 400合金丝材的再结晶过程及力学性能的影响 |
| |
| 引用本文： | 张涛,郑文杰,李才巨.冷拔后退火对Monel 400合金丝材的再结晶过程及力学性能的影响[J].金属热处理,2022,47(1):56-62. |
| |
| 作者姓名： | 张涛 郑文杰 李才巨 |
| |
| 作者单位： | 1.昆明理工大学 材料科学与工程学院, 云南 昆明 650039;2.钢铁研究总院 特殊钢研究院, 北京 100081 |
| |
| 摘 要： | 使用ETM105D电子拉伸试验机对退火后的Monel 400合金丝材进行拉伸试验,并通过Matlab-MTEX软件统计再结晶体积分数的方法,研究了冷拔态Monel 400合金丝材在不同退火处理后的组织演变、力学性能及二者的关系,构建了Monel 400合金的再结晶模型,并计算其再结晶激活能。结果表明,用Matlab-MTEX软件处理EBSD数据得到的图像可以直观地呈现试样在经历退火处理后组织中晶粒的演变,以及更准确地统计再结晶的体积分数;选择825 ℃×20 min退火,可以获得较好的塑性和足够的强度。
|
| 关 键 词： | Monel400合金丝材 再结晶 MTEX 激活能 |
| 收稿时间： | 2021-07-05 |
Effect of annealing after cold drawing on mechanical properties and recrystallization process of Monel 400 alloy wire |
| |
| Zhang Tao,Zheng Wenjie,Li Caiju.Effect of annealing after cold drawing on mechanical properties and recrystallization process of Monel 400 alloy wire[J].Heat Treatment of Metals,2022,47(1):56-62. |
| |
| Authors: | Zhang Tao Zheng Wenjie Li Caiju |
| |
| Affiliation: | 1. Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming Yunnan 650039, China;2. Research Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China |
| |
| Abstract: | Tensile test of annealed Monel 400 alloy wire was carried out by using ETM105D electronic tensile testing machine, and the microstructure evolution, mechanical properties and their relationship of the cold drawn Monel 400 alloy wire after different annealing treatments were studied by using Matlab-MTEX software to calculate recrystallization volume fraction. The results show that the image obtained by processing EBSD data with Matlab-METX software can intuitively present the evolution of grain in the specimen after annealing treatment, and more accurate statistics of the volume fraction of recrystallization. Good plasticity and sufficient strength can be obtained by annealing at 825 ℃ for 20 min. |
| |
| Keywords: | Monel 400 alloy wire recrystallization MTEX activation energy |
| 本文献已被 维普 万方数据 等数据库收录！ |
| 点击此处可从《金属热处理》浏览原始摘要信息 |
|
点击此处可从《金属热处理》下载全文 |
|