Waterborne polyurethane-silanized CoFe2O4-acrylate magnetic pressure-sensitive adhesive |
| |
| Authors: | Heqing Fu Weifeng Chen Xiaoya Li Rong Wang |
| |
| Affiliation: | School of Chemistry and Chemical Engineering, South China University of Technology, Guangzhou, China |
| |
| Abstract: | A novel waterborne polyurethane-silanized CoFe2O-acrylate magnetic pressure-sensitive adhesive was prepared. With the increase of PU content, gel content, swelling capability, and SAFT increased, and fracture energy increased first, then decreased. The T-peeling strength increased from 8.93 to 19.07 N · m?1, tack force increased from No.3 to No.10, while shear resistance increased from 35 to 72 h, and then they decreased. Two empirical models: WA = 90.46 + 125.04PU]-319.96PU]2 and T = 9.09 + 96.07PU]-235.11PU]2, were obtained. With the increase of CoFe2O4 content, the saturation magnetization increased from 5.5 to 14.2 emu · g?1, and remanence increased from 1.7 to 3.7 emu · g?1, while coercivity decreased from 875 to 763 Oe. |
| |
| Keywords: | Dynamic mechanic properties magnetic properties polyurethane pressure-sensitive adhesive silanized CoFe2O4 |
|
|