| 摘 要： | Five different compositions of K x V 2 O 5 ·nH 2 O(where x=0.00,0.0017,0.0049,0.0064 and 0.0091 mol) were prepared by the sol-gel process.Electrical conductivity and thermoelectric power were measured parallel to the substrate surface in the temperature range of 300-480 K.The electrical conductivity showed that all samples were semiconductors and that conductivity increased with increasing K content.The conductivity of the present system was primarily determined by hopping carrier mobility.The carrier density was evaluated as well.The conduction was confirmed to obey non-adiabatic small polaron hopping.The thermoelectric power or Seebeck effect,increased with increasing K ions content.The results obtained indicated that an n-type semiconducting behavior within the temperature range was investigated.
|