NOx adsorption on MnO2/NaY composite: an in situ FTIR and EPR study

The NO, NO/O₂, and NO/O₂/H₂O adsorption on MnO₂/NaY (5 and 15 wt.% MnO₂) composite catalyst and NaY has been studied by means of in situ FTIR and EPR spectroscopy at elevated temperatures and during heating under reaction-like conditions. NO adsorption and co-adsorption of NO and O₂ on NaY and MnO₂/NaY proceeds via oxidation of NO forming NO₂⁻ and NO₃⁻ species. Whereas the manganese dioxide preferably acts as oxidising agent, the zeolite stores the NO_x species as nitrite and nitrate ions in the solid. In the presence of oxygen, the nitrate formation is enhanced due to additional oxidation of NO through gaseous oxygen leading to NO₂. Dimerisation of NO₂ to N₂O₄ and following disproportionation of the latter causes the formation of NO⁺ and NO₃⁻ species which are associated with nucleophilic zeolitic oxygen and especially alkali cations of the zeolite, respectively. The presence of oxygen facilitates reoxidation of Mn²⁺ which keeps more Mn ions in the active state. Pre-adsorbed water and higher amounts of water vapour in the feed hinder the NO adsorption by blocking the adsorption sites and shift the nitrate formation to higher temperatures. The quantities and thermal stability of the nitrates formed during NO and NO/O₂ adsorption differs which points to a different mechanism of nitrate formation. In the absence of gaseous oxygen, nitrates are formed by participation of only lattice oxygen. In the presence of oxygen, nitrate formation by dimerisation and disproportionation reactions of NO₂ dominates. The manganese component of the composite catalyst supports the oxidation of NO to nitrite and subsequently to nitrate. During this process Mn⁴⁺ is reduced to Mn²⁺ as evidenced by in situ EPR measurements.