Investigations of Compositions and Performance of PtRuMo/C Ternary Catalysts for Methanol Electrooxidation
Authors:Zhen‐Bo Wang  Peng‐Jian Zuo  Ge‐Ping Yin
Abstract:PtRuMo/C catalyst was prepared by impregnation reduction method and characterised. Comparison is made between a home‐made PtRu/C prepared by similar method and Pt/C (E‐Tek Co., Pt/C‐ET) catalysts. One glassy carbon disc electrode for ternary alloy catalyst was used to evaluate the catalytic performances by cyclic voltammetric, chronoamperometric, amperometric i–t curves, and electrochemical impedance spectra (EIS). The electrochemical measurement results indicated that the performance of PtRuMo/C with a molar ratio of 6:3:1 was the highest among 15 PtxRuyMo10–xy/C catalysts with different molar ratios. The composition, particle size, lattice parameter and morphology of the PtRuMo(6:3:1)/C catalyst were determined by means of X‐ray energy dispersive analysis, X‐ray diffraction (XRD) and transmission electron micrographs (TEM). The result of XRD analysis exhibits that PtRuMo(6:3:1)/C has the fcc structure with the smaller lattice parameter than the home‐made PtRu/C and Pt/C‐ET. Its typical particle sizes is only about 5 nm. With respect to the catalytic activity and stability, the PtRuMo(6:3:1)/C catalyst is superior to PtRu/C despite their comparable active areas. Though the electrochemically active surface area of Pt/C‐ET is the biggest, its performance is the lowest. EIS results also indicate that the reaction resistances for methanol electrooxidation on the PtRuMo(6:3:1)/C catalyst are smaller than those of PtRu/C at different polarisation potentials.
Keywords:Composition Investigation  Direct Methanol Fuel Cell  Methanol Electrooxidation  Pt‐Ru/C catalyst  PtRuMo/C catalyst
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号