Healing of double oxide film defects in A356 aluminium melt |
| |
| Authors: | Majid Aryafar Ramin Raiszadeh and Alireza Shalbafzadeh |
| |
| Affiliation: | (1) Department of Metallurgy and Materials Science, School of Engineering, Shahid Bahonar University of Kerman, Jomhoori Eslami Blvd., Kerman, Iran;(2) Materials Department, International Center for Science, High Technology and Environmental Sciences, Mahan, Kerman, Iran; |
| |
| Abstract: | The possibility of the bonding of the two layers of a double oxide film defect when held in liquid A356 Al alloy was investigated.
The defect was modelled experimentally by maintaining two aluminium oxide layers in contact with each other and the atmosphere
trapped between them in the A356 liquid alloy for varying lengths of time of between 30 s and 48 h. Any changes in the composition
and morphology of these layers were studied by SEM, EDX and XRD. The results showed that the two layers of a double oxide
film defect might bond to each other by two different mechanisms, one during the transformation of Al2O3 to MgAl2O4 spinel in relatively short holding times, which would cause the layers to bond at several points and the other during the
gradual transformation of spinel to MgO in longer times, which would cause strong bonding between the layers. It was shown
that any bonding can take place essentially only after the oxygen and nitrogen of the atmosphere within the defect are consumed. |
| |
| Keywords: | |