Poly(hydroxyethyl methacrylate) nanobeads containing imidazole groups for removal of Cu(II) ions

Poly(hydroxyethyl methacrylate) (PHEMA) nanobeads with an average size of 300 nm in diameter and with a polydispersity index of 1.156 were produced by a surfactant free emulsion polymerization. Specific surface area of the PHEMA nanobeads was found to be 996 m²/g. Imidazole containing 3-(2-imidazoline-1-yl)propyl(triethoxysilane) (IMEO) was used as a metal-chelating ligand. IMEO was covalently attached to the nanobeads. PHEMA-IMEO nanobeads were used for the removal of copper(II) ions from aqueous solutions. To evaluate the degree of IMEO loading, the PHEMA nanobeads were subjected to Si analysis by using flame atomizer atomic absorption spectrometer and it was estimated as 973 µmol IMEO/g of polymer. The PHEMA nanobeads were characterized by transmission electron microscopy and fourier transform infrared spectroscopy. Adsorption equilibrium was achieved in about 8 min. The adsorption of Cu²⁺ ions onto the PHEMA nanobeads was negligible (0.2 mg/g). The IMEO attachment into the PHEMA nanobeads significantly increased the Cu²⁺ adsorption capacity (58 mg/g). Adsorption capacity of the PHEMA-IMEO nanobeads increased significantly with increasing concentration. The adsorption of Cu²⁺ ions increased with increasing pH and reached a plateau value at around pH 5.0. Competitive heavy metal adsorption from aqueous solutions containing Cu⁺, Cd²⁺, Pb²⁺ and Hg²⁺ was also investigated. The adsorption capacities are 61.4 mg/g (966.9 µmol/g) for Cu²⁺; 180.5 mg/g (899.8 µmol/g) for Hg²⁺; 34.9 mg/g (310.5 µmol/g) for Cd²⁺ and 14.3 mg/g (69 µmol/g) for Pb²⁺. The affinity order in molar basis is observed as Cu²⁺ > Hg²⁺ > Cd²⁺ > Pb²⁺. These results may be considered as an indication of higher specificity of the PHEMA-IMEO nanobeads for the Cu²⁺ comparing to other ions. Consecutive adsorption and elution operations showed the feasibility of repeated use for PHEMA-IMEO nanobeads.