| 废纸浆增强玉米淀粉基复合材料的制备及其力学性能研究 |
| |
| 引用本文： | 曾广胜,林瑞珍,郑良杰,陈磊,孟聪.废纸浆增强玉米淀粉基复合材料的制备及其力学性能研究[J].功能材料,2012,43(16):2218-2221. |
| |
| 作者姓名： | 曾广胜 林瑞珍 郑良杰 陈磊 孟聪 |
| |
| 作者单位： | 1. 湖南工业大学包装新材料与技术中国包装总公司重点实验室,湖南株洲412008 湖南：[业大学先进包装材料与技术湖南省普通高校重点实验室,湖南株洲412008
2. 湖南工业大学包装新材料与技术中国包装总公司重点实验室,湖南株洲412008 广西大学有色金属及材料加工新技术国家重点实验室,广西南宁530000 |
| |
| 基金项目： | 基金项目:国家自然科学基金资助项目，湖南省科技厅科技计划资助项目 |
| |
| 摘 要： | 以甘油和尿素作为混合塑化剂、废纸浆为增强体,玉米淀粉、聚乙烯醇为基体,利用熔融共混法制备了废纸浆增强玉米淀粉复合材料。研究了混合增塑剂、废纸浆、水含量、氢氧化钠浓度对复合材料力学性能的影响。力学性能测试结果表明,甘油和尿素混合塑化剂对复合材料有反增塑作用,当甘油/尿素含量分别为10/20份时,拉伸强度最佳为10.26MPa;氢氧化钠浓度为4%时,复合材料综合力学性能最好;废纸浆对复合材料有增强作用,当含量为35份时,拉伸强度最佳为11.35MPa;随着含水率的增加,材料的拉伸强度降低,断裂伸长率先增加后降低;扫描电镜观察发现,甘油和尿素混合塑化剂能够增塑淀粉,很好的改善废纸浆和玉米淀粉之间的相容性。
|
| 关 键 词： | 废纸浆 玉米淀粉 氢氧化钠 力学性能 相容性 |
Preparation and performance study of waste paper pulp reinforced cornstarch-based composites |
| |
| ZENG Guang-sheng,LIN Rui-zhen,ZHENG Liang-jie,CHEN Lei,MENG Cong.Preparation and performance study of waste paper pulp reinforced cornstarch-based composites[J].Journal of Functional Materials,2012,43(16):2218-2221. |
| |
| Authors: | ZENG Guang-sheng LIN Rui-zhen ZHENG Liang-jie CHEN Lei MENG Cong |
| |
| Affiliation: | 1,2(1.Key Laboratory of New Materials and Technology for Packaging of China National Packaging Corporation, Hunan University of Technology,Zhuzhou 412008,China; 2.Key Laboratory of Advanced Materials and Technology for Packaging of Hunan Universities, Hunan University of Technology,Zhuzhou 412008,China; 3.Key Laboratory of New Processing Technology for Materials and Non ferrous Metal, Ministry of Education,Guangxi University,Nanning 530000,China) |
| |
| Abstract: | The waste paper pulp /cornstarch-based composites plasticized by a mixed plasticizer of glycerol and urea,strengthened by waste paper pulp were obtained from cornstarch and PVA by means of the melting processing method.The influence of mixed plasticizer content,NaOH concentration,waste paper pulp and water content in the mechanical properties of composites were studied.The results show that mixed plasticizer has an antiplastic effect on the composites.When the glycerol and urea content is respectively15phr,mechanical properties of composites could get a good performance.Waste paper pulp do improve the mechanical properties of composites,tensile strength of composites has the highest value when waste paper pulp content is 35phr.Tensile strength of composites is increased with the increasing water content,then it decreased.While,the behavior of elongation at break of composites is contrary.The SEM micrographs of the cornstarch granule,thermoplastic cornstarch plasticized by the mixed plasticizer were observed.The results reveal that the mixed plasticizer could plasticize the cornstarch and the compatibility between cornstarch and waste paper pulp is obviously improved. |
| |
| Keywords: | waste paper pulp cornstarch NaOH mechanical property compatibility |