Microcracking in B4C-TiB2 Composites

Boron carbide/titanium diboride composites with 20 and 40 vol% particulate TiB₂ and various amounts of free carbon were investigated with respect to microcrack toughening. In agreement with previous work, the mere addition of TiB₂ was found to raise the toughness from 2.2 MPa·m^1/2 up to 3.0 and 3.5 MPa·m^1/2, respectively. A further and very significant increase of composite toughness up to 6.0 MPa·m^1/2 was discovered upon the incorporation of free carbon. SEM and TEM observations reveal that this toughening is associated with microcracking at B₄C-TiB₂ phase boundaries. Microcracking is triggered by thin carbon interlayers, which are located at hetero interfaces and supply a weak fracture path.