Effects of surface roughness of substrates on the c-axis preferred orientation of ZnO films deposited by r.f. magnetron sputtering

The c-axis preferred orientation of ZnO film is the most important factor for its successful application in piezoelectric devices. The effects of surface roughness of the substrate on the c-axis preferred orientation of ZnO thin films, deposited by radio frequency magnetron sputtering, were investigated. During sputtering, the oxygen content in the argon environment used was varied from 0 to 70% at a total sputtering pressure of 10 mTorr. Very smooth Si, smooth evaporated Au/Si, smooth evaporated-Al/Si, and rough sputtered-Al/Si were used as substrates. Their r.m.s. roughnesses, as measured by atomic force microscopy, were 1.27, 17.1, 21.1 and 65-118 Å, respectively. The crystalline structure and the angular spread of the (0 0* 2) plane normal to the ZnO films were determined using X-ray diffraction and X-ray rocking curves, respectively. The crystallinity and the preferred c-axis orientation of the ZnO films were strongly dependent on the surface roughness of the substrates rather than on the oxygen content of the working environment or on the chemical nature of the substrate.