Phase-transition temperatures and piezoelectric properties of (Bi/sub 1/2/Li/sub 1/2/)TiO/sub 3/-(Bi/sub 1/2/K/sub 1/2/)TiO/sub 3/ lead-free ferroelectric ceramics

The phase-transition temperatures and piezoelectric properties of x(Bi_1/2Na_1/2)TiO_3-y(Bi_1/2Li_1/2)TiO_3-z(Bi_1/2K_1/2)TiO₃ x + y + z = 1] (abbreviated as BNLKT100y-100z) ceramics were investigated. These ceramics were prepared using a conventional ceramic fabrication process. The phase-transition temperatures such as depolarization temperatures T_d, rhombohedral-tetragonal phase transition temperature T_R-T, and dielectric-maximum temperature T_m were determined using electrical measurements such as dielectric and piezoelectric properties. The X-ray powder diffraction patterns of BNLKT100y-100z show the morphotropic phase boundary (MPB) between rhombohedral and tetragonal at approximately z = 0.20, and the piezoelectric properties show the maximum at the MPB. The electromechanical coupling factor &33, piezoelectric constant d₃₃ and T_d of BNLKT4-20 and BNLKT8-20 were 0.603, 176 pC/N, and 171degC, and 0.590, 190 pC/N, and 115degC, respectively. In addition, the relationship between d₃₃ and T_d of tetragonal side and rhombohedral side for BNLKT4-100z and BNLKT8-100z were presented. Considering both high T_d and high d₃₃, the tetragonal side of BNLKT4-100z is thought to be the superior composition. The d₃₃ and T_d of BNLKT4-28 were 135 pC/N and 218degC, respectively. Moreover, this study revealed that the variation of Td is related to the variation of lattice distortion such as rhombohedrality 90-alpha and tetragonality c/a.