Effect of cobalt doping on ceria-zirconia mixed oxide: Structural characteristics, oxygen storage/release capacity and three-way catalytic performance |
| |
作者姓名: | 王建强 沈美庆 王军 高继东 马杰 刘双喜 |
| |
作者单位: | [1]Key Laboratory.liar Green Chemical Technology of State Education Ministry, School of Chemical Engineering & Technology, Tianjin University, Tianjin 300072, China [2]China Automotive Technology & Research Center, Tianjin 300162, China |
| |
基金项目: | Foundation item: Project supported by National High-Tech Research and Development Program of China (201 IAA03A405) and the Key Program of Tianjin Natural Science Foundation (09JCZDJC26600) |
| |
摘 要: | The effect of Co doping on ceria-zirconia mixed oxides was investigated for Co 0.1 Ce 0.6 Zr 0.3 O x sample prepared by sol-gel method. The Pd-only three-way catalyst (TWC) was obtained by incipient wetness impregnation with 0.5 wt.% Pd loading. The structural and oxygen handling properties were analyzed by X-ray diffraction (XRD), H 2 -temperature programmed reduction (H 2 -TPR) and the dynamic oxygen storage capacity (DOSC). The introduction of Co into ceria-zirconia lattice strongly modified the mobility of oxygen and enhanced the DOSC performance. Pd-only TWC based on the Co 0.1 Ce 0.6 Zr 0.3 O x support exhibited superior activity for water-gas shift and steam reforming and amplified amplitude of stoichiometric window.
|
关 键 词: | three-way catalyst stoichiometric window dynamic oxygen storage capacity water-gas shift steam reforming Co doping rare earths |