Thermoelectric properties of Yb x Co_4 Sb_(12) system |
| |
引用本文: | 刘洪权,赵新兵,朱铁军,谷亦杰.Thermoelectric properties of Yb x Co_4 Sb_(12) system[J].中国稀土学报(英文版),2012,30(5):456-459. |
| |
作者姓名: | 刘洪权 赵新兵 朱铁军 谷亦杰 |
| |
作者单位: | [1]College of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, China [2]Department of Materials Science, State Key Laboratory of Silicon Materials, Zhejiang University, Hangzhou 31002 7, China |
| |
基金项目: | supported by National Natural Science Foundation of China (50801054);the Research Award Fund for Outstanding Young Scientist in Shandong Province,China (BS2011CL031) |
| |
摘 要: | Yb x Co 4 Sb 12 polycrystals were fabricated by vacuum melting combined with hot-press sintering.The effect of Yb-filling on thermoelectric property of unfilled skutterudite CoSb 3 was investigated,which indicated the enhancement of the power factor of the material.Transport properties of materials changed from semi-conductor to semi-metal during the measurement of electrical conductivity,which indicated the change of electronic band structure.The maximum value of electrical conductivity was about 190000 S/m at 300 K for all samples.On the basis of Yb-filling,power factor of Yb 0.2 Co 4 Sb 12 reached 5-6 mW/(m·K) during the measurement temperature.Thermal conductivity decreased with increase of Yb content,and the thermal conductivity of Yb 0.2 Co 4 Sb 12 reached 3.2 W/(m·K) at 600 K.The ZT value of Yb 0.2 Co 4 Sb 12 reached 1.16 at 700 K due to positive contribution from high power factor and low thermal conductivity.
|
关 键 词: | thermoelectric properties power factor Yb-filling thermal conductivity rare earths |