Effects on mechanical properties in electron beam welding of TC4 alloy by laser shock processing
Authors:Lu Jinzhong    Zhang Yongkang    Kong Dejun    Ren Xudong    Ge Tao   Zou Shikun
Affiliation:(1) School of Mechanical Engineering, Jiangsu University, Zhenjiang, 212013, China;(2) Beijing Aeronautical Manufacturing Technology Research Institute, Beijing, 100024, China
Abstract:The surface of TC4 titanium alloy welding line by electron beam welding (EBW) was processed by high power Q-switched and repetition-rate Nd: glass laser. Effects of laser power and spot diameter on residual stress and microhardness of the TC4 alloy welding line by laser shock processing (LSP) have been analyzed. Results show that residual stresses almost do not change as laser power is 45.9 J, spot diameter is ϕ9 mm; While laser power is 45.9 J, spot diameter less than ϕ3 mm, the distribution of residual stress in welding line occurs obvious variation, which residual stress increase obviously with spot diameter decrease. When power density is bigger than 1.8 × 1010 W/cm2, residual stresses of electron beam welding line occur change by LSP, which improve obviously residual stress distribution; while laser power is bigger than 1.2 × 1010 W/cm2, the surface micro-hardness of electron beam welding line occurs change by LSP, which improve obviously micro-hardness distribution. Mechanical properties of TC4 titanium alloy welding line will be improved by LSP, which provides experimental foundation for further controlling the distributions of residual stress and micro-hardness during laser shock processing. __________ Translated from Journal of Jiangsu University (Natural Science), 2006, 27(3): 207–210 [译自: 江苏大学学报 (自然科学版)]
Keywords:laser shock processing (LSP)  repetition-rate laser  TC4 alloy  electron beam welding  residual stress  micro-hardness
本文献已被 万方数据 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号