Influence of sintering temperature on secondary phases formation and microwave dielectric properties of Ca2Ce2Ti5O16 ceramics

Ca₂Ce₂Ti₅O₁₆ dielectric ceramics prepared by conventional solid-state ceramic route was investigated. Phase composition and microwave dielectric properties were measured using XRD and Vector network analyzer, respectively. XRD analysis of the calcined and sintered samples revealed the formation of CeO₂ and another unidentified phase (that vanished at ? 1400 °C) as secondary phases along with the parent Ca₂Ce₂Ti₅O₁₆ phase. The amount of the parent Ca₂Ce₂Ti₅O₁₆ phase increased with increasing sintering temperature from 1350 °C to 1450 °C accompanied by a decrease in the apparent density. The density decreased but ? _r and Q _u f _o increased with sintering temperature. An ? _r ～ 81.5, Q _u f _o ～ 5915 GHz and τ _f ～ 219 GHz were achieved for the sample sintered at 1450 °C.