AFeO3 (A=La, Nd, Sm) and LaFe1−xMgxO3 perovskites as methane combustion and CO oxidation catalysts: structural, redox and catalytic properties

Catalytic methane combustion and CO oxidation were investigated over AFeO₃ (A=La, Nd, Sm) and LaFe_1?xMg_xO₃ (x=0.1, 0.2, 0.3, 0.4, 0.5) perovskites prepared by citrate method and calcined at 1073 K. The catalysts were characterized by X-ray diffraction (XRD). Redox properties and the content of Fe⁴⁺ were derived from temperature programmed reduction (TPR). Specific surface areas (SA) of perovskites were in 2.3–9.7 m² g^?1 range. XRD analysis showed that LaFeO₃, NdFeO₃, SmFeO₃ and LaFe_1?xMg_xO₃ (x·0.3) are single phase perovskite-type oxides. Traces of La₂O₃, in addition to the perovskite phase, were detected in the LaFe_1?xMg_xO₃ catalysts with x=0.4 and 0.5. TPR gave evidence of the presence in AFeO₃ of a very small fraction of Fe⁴⁺ which reduces to Fe³⁺. The fraction of Fe⁴⁺ in the LaFe_1?xMg_xO₃ samples increased with increasing magnesium content up to x=0.2, then it remained nearly constant. Catalytic activity tests showed that all samples gave methane and CO complete conversion with 100% selectivity to CO₂ below 973 and 773 K, respectively. For the AFeO₃ materials the order of activity towards methane combustion is La>Nd>Sm, whereas the activity, per unit SA, of the LaFe_1?xMg_xO₃ catalysts decreases with the amount of Mg at least for the catalysts showing a single perovskite phase (x=0.3). Concerning the CO oxidation, the order of activity for the AFeO₃ materials is Nd>La>Sm, while the activity (per unit SA) of the LaFe_1?xMg_xO₃ catalysts decreases at high magnesium content.