Microstructure and Mechanical Properties of Mg-7Al-2Sn Alloy Processed by Super Vacuum Die-Casting

The microstructural evolution of Mg-7Al-2Sn (AT72) alloy processed by super vacuum die-casting and heat treated at various conditions was studied. The results showed that the dendritic microstructure in the as-cast AT72 alloy consisted of α-Mg, Mg₂Sn, and Mg₁₇Al₁₂ phases. After solution treatment at temperatures ranging from 663 K to 703 K (390 °C to 430 °C), the Mg₁₇Al₁₂ phase dissolved into the Mg matrix entirely, while the Mg₂Sn phase partially dissolved into matrix. An average grain size of about 40 μm in the alloy could be achieved after solution treatment at 683 K (410 °C) for 16 hours. A large amount of lath-shaped precipitates of Mg₂Sn and Mg₁₇Al₁₂ was observed in the aged AT72 alloy. The results of tensile property evaluation at room temperature showed that the ductility of the solution-treated alloy was dramatically improved, in comparison with the as-cast alloy. In the peak aged condition, the tensile strength of the alloy was increased, which was attributed to the deposition of fine Mg₁₇Al₁₂ and Mg₂Sn precipitates during the aging treatment.