Diffusion in β2 Fe-Ni-Al alloys |
| |
Authors: | T. D Moyer M. A. Dayananda |
| |
Affiliation: | 1. E. I. Dupont de Nemours & Co., Jackson Laboratory, 19898, Wilmington, DE 2. School of Materials Engineering, Purdue University, 47907, W. Lafayette, IN
|
| |
Abstract: | Diffusion in the β(bcc) phase field of the Fe-Ni-Al system was investigated at 1004°C with solid-solid diffusion couples assembled with β2 alloys of selected composition. Experimental diffusion paths were determined for all couples and interdiffusion coefficients calculated at composition points corresponding to intersections of diffusion paths and maxima and minima of concentration profiles. The dependence of interdiffusion coefficients on composition was most clearly presented in terms of the parameter Fe/(Fe + Ni). The diffusive interactions between aluminum and nickel as represented by the cross coefficients were either positive or negative depending on the ternary composition. The Fe/(Fe + Ni) ratio appeared to be a significant parameter since iron and nickel atoms behave differently in affecting the degree of ordering in nonstoichiometric (Fe, Ni)Al alloys with less than 50 at. pct aluminum. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|