High ionic conductivity in CeO2 SOFC solid electrolytes; effect of Dy doping on their electrical properties |
| |
| Affiliation: | 1. Tecnológico Nacional de México, Instituto Tecnológico de Saltillo, 25280, Saltillo, Coahuila, Mexico;2. CIQA, Enrique Reyna Hermosillo 140, 25294, Saltillo, Coahuila, Mexico;3. COMIMSA-Conacyt, Ciencia y Tecnología 790, 25290, Saltillo, Coahuila, Mexico;4. CINVESTAV Unidad Saltillo, Av. Industria Metalúrgica 1062, 25900, Ramos Arizpe, Coahuila, Mexico;5. INEEL, Reforma 113, 62490, Cuernavaca, Morelos, Mexico;1. Department of Chemical Engineering, Indian Institute of Technology, New Delhi 110016, India;2. Department of Applied Physics, Aalto University, P. O. Box 15100, 00076, Finland;1. School of Materials Science and Physics, China University of Mining and Technology, Xuzhou, 221116, China;2. Key Laboratory of Gas and Fire Control for Coal Mines, Ministry of Education, China University of Mining and Technology, Xuzhou, 221116, China;3. School of Physics and Materials Science, Anhui University, No. 111 Jiulong Road, Hefei, 230601, China;1. School of Metallurgy, Northeastern University, Shenyang, 110819, China;2. Liaoning Key Laboratory for Metallurgical Sensor and Technology, Northeastern University, Shenyang, 110819, China;3. Institute of Advanced Material Technology, Northeastern University, Shenyang, 110819, China;1. Department of Physics, Osmania University, Hyderabad 500007, Telangana, India;2. Methodist College of Engineering and Technology, Hyderabad 500001, Telangana, India |
| |
| Abstract: | Ionic conductors composed of lanthanide-doped ceria with general formula DyyCe1-yO2-δ (y = 0.05, 0.1 and 0.15) were synthesized by mechanochemistry (mechanical milling), and their electrical properties analyzed to be used as solid electrolytes in low-temperature SOFC. Starting oxide reagents were milled at different times in a planetary mill and the evolution of their structures and phases with milling time and temperature (up to 1500 °C) was followed by XRD. Just milled powders were also uniaxially pressed and sintered at different temperatures (1200, 1350 and 1500 °C), and analyzed by FE-SEM, to explore their morphologies as a function of temperature and Dy content. The electrical properties of these materials and undoped commercial CeO2 were analyzed by impedance spectroscopy at different temperatures (200–650 °C) and frequencies (100 Hz - 1 MHz). Results showed that mechanochemistry is a suitable method to obtain the DyyCe1-yO2-δ systems after 20 h of milling, since XRD patterns of these milled powders reveal the formation of fluorite-type cubic solid solutions for all studied compositions. Increasing of temperature generates a higher crystallinity in these materials while the absence of phase transitions in them is corroborated at 1200 °C. Analysis of electrical properties of samples sintered a 1200 °C corroborates the viability of these systems to be used as solid electrolytes in the SOFC technology, being that high dc conductivities (σdc) were obtained for all doped samples, especially for the composition Dy0.1Ce0·9O2-δ, which showed a σdc = 1 × 10−1.91 S cm−1 at 650 °C. This value represents an increase of almost three orders of magnitude for this composition with respect to the undoped CeO2 sample (y = 0, σdc = 1 × 10 −4.83 Scm−1). |
| |
| Keywords: | SOFC Doped ceria Ionic conductors Solid electrolytes Mechanical milling |
| 本文献已被 ScienceDirect 等数据库收录！ |
|