低熔点共聚酯序列结构分析 |
| |
引用本文: | 邓丽娜,王彦芳,刘灯胜,李文刚. 低熔点共聚酯序列结构分析[J]. 合成纤维, 2018, 0(4): 1-7 |
| |
作者姓名: | 邓丽娜 王彦芳 刘灯胜 李文刚 |
| |
作者单位: | 东华大学材料科学与工程学院 |
| |
摘 要: | 采用PTA路线合成一系列低熔点共聚酯,在不改变其它条件的基础下,通过改变单体的配比,将所获得的聚合物的熔点控制在110℃左右。利用核磁共振对聚合物的序列结构进行表征,发现所制得的聚合物的无规度均接近1,表明所得共聚酯均接近无规共聚物。
|
关 键 词: | 低熔点共聚酯 序列结构 核磁共振 无规度 |
The Sequence Structure of the Low Melting Point Copolyester |
| |
Affiliation: | ,College of Materials Science and Engineering, Donghua University |
| |
Abstract: | A series of low melting point copolyesters were synthesized by PTA route. The melting point ofthe obtained polymer was controlled at about 110 ℃ by changing the monomer ratio without changing theother conditions. NMR was used to characterize the sequence structure of the polymers. It is found that theprepared polymers all have a randomness close to 1, that indicates the resulting copolyesters are close torandom copolymers. |
| |
Keywords: | low melting point copolyester sequence structure NMR randomness |