High‐temperature low cycle fatigue damage assessment in near alpha IMI‐834 titanium alloy

In the present work, evolution of damage under high‐temperature (823 K) low cycle fatigue loading condition in near α IMI‐834 titanium alloy has been studied. The in situ damage has been experimentally measured during cyclic deformation using the alternating current potential drop (ACPD) technique. The measured damage curve has been compared with the damage curves calculated through mechanical variables such as cyclic modulus and stress amplitude. The ACPD damage curve has been found most sensitive towards high‐temperature low cycle fatigue damage evolution.