Processing and Electromechanical Properties of (Bi0.5Na0.5)(1−1.5x)LaxTiO3 Ceramics

Bismuth sodium titanate (Bi_0.5Na_0.5TiO₃, BNT) with 0–6 at.% lanthanum was prepared by the conventional mixed oxide method. Each composition was calcined at 800–900°C for 2–5 h to form a pure perovskite phase. Green pellets were sintered at 1050–1150°C for 1–4 h to obtain dense ceramics with at least 95% of theoretical density. X–ray diffraction (XRD) showed phase distortion as lanthanum was added to this system. Meanwhile, a small amount of La was found to affect the grain size and had an influence on the poling conditions and electrical properties. The BNT–based composition with 1 at.% La doping provided a dielectric constant ( K ) of 560, a piezoelectric charge constant ( d ₃₃) of 92 pC/N, and a hydrostatic piezoelectric coefficient ( d _h) of 72 pC/N.