| Abstract: | To study the effect of dispersed poly(butadiene-co-acrylonitrile) (NBR) rubber size on the physical properties of poly(styrene-co-acrylonitrile) (SAN)/NBR blends, SANs with various melt viscosities and acrylonitrile (AN) contents were examined. The dispersed size of NBR, whose AN content is 30 wt %, was reduced as the melt viscosity of the SAN matrix was increased or as the AN content of the SAN matrix was reduced in the range of 19–32 wt %. As the melt viscosity of the SAN matrix was increased, the damping peak of the NBR phase moved to a higher temperature, and as the AN content of SAN was reduced, the damping peak of the SAN phase moved to a lower temperature. Higher values of impact strength and elongation at break and reduced yield behavior at a low shear rate were observed at a finer dispersion of NBR. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 73: 935–941, 1999 |