Sintering of Colloidal Ru/γ-Al2O3 Catalyst in Hydrogen

Colloidal 5.1 wt% Ru/γ-Al₂O₃ catalyst was prepared by a microwave assisted, solvothermal reduction of RuCl₃ in ethylene glycol in the presence of γ-Al₂O₃. The catalyst subjected to heat-treatment in hydrogen up to 700 °C, was characterized by BET, XRD, TEM and H₂ chemisorption. As-prepared catalyst contained Ru nanoparticles with mean size of 1.5 nm and narrow size distribution uniformly distributed over the support. The nanoparticles were stable on the alumina to 500 °C, but treatment at 600–700 °C caused some sintering of Ru due to migration and coalescence of a part of smallest ruthenium nanoparticles. However, even after H₂ treatment at 700 °C, large amount of Ru nanoparticles with sizes of 1–3 nm remained in the catalyst. H₂ chemisorption data revealed decrease of Ru dispersion from 0.28 to 0.19 by hydrogen treatment at 700 °C and were in good correspondence with TEM results. On the contrary, mean crystallite sizes obtained from XRD were strongly overestimated.