| 压缩机供液泵叶片失效分析 |
| |
| 引用本文： | 秦炎锋,魏中坤,关凯书.压缩机供液泵叶片失效分析[J].流体机械,2014(10):60-63. |
| |
| 作者姓名： | 秦炎锋 魏中坤 关凯书 |
| |
| 作者单位： | 华东理工大学,上海,200237 |
| |
| 摘 要： | 采用化学成分分析、力学性能测试、断口扫描电镜观察和金相观察等失效分析手段,对压缩机供液泵的叶片断裂原因进行分析,并对未断裂叶片根部进行表面着色探伤和金相组织观察。结果表明:叶片断裂原因是因为根部存在应力腐蚀裂纹,这些裂纹成为疲劳断裂的起源位置。
|
| 关 键 词： | 供液泵叶片 疲劳断裂 失效分析 应力腐蚀裂纹 |
Failure Analysis of Liquid Ring Compressor Service Liquid Pump Bladez |
| |
| QIN Yan-feng,WEI Zhong-kun,GUAN Kai-shu.Failure Analysis of Liquid Ring Compressor Service Liquid Pump Bladez[J].Fluid Machinery,2014(10):60-63. |
| |
| Authors: | QIN Yan-feng WEI Zhong-kun GUAN Kai-shu |
| |
| Affiliation: | ,East China University of Science and Technology |
| |
| Abstract: | The fracture of liquid ring compressor service liquid pump blade was analyzed by means of chemical composition analyzed,mechanical property test,SEM and metallogriphic,and the root of whole blade was analyzed by means of surface penetrant and metallographic. The result shows that,the cause of fracture blade was the existence of the stress- corrosion crack,and the crack caused the main courses of fatigue fracture. |
| |
| Keywords: | service liquid pump blade failure analysis fatigue fracture stress corrosion crack |