Catalytic activity and control of the nascent morphology of polyethylenes obtained with first and second generation of Ziegler–Natta catalysts

The morphologies of the as-produced polyethylenes obtained by slurry polymerization process of ethylene in n-heptane, using heterogeneous conventional and supported Ziegler–Natta catalysts, were investigated. The ability of four different catalytic systems in controlling the size and shape of the nascent polymer particles were tested. The catalytic systems employed were: the original Ziegler type catalyst produced by reduction of TiCl₄ with Et₂AlCl, the Natta type catalyst TiCl₃–AA, the reduced TiCl₄ with the metal carbonyls Mo(CO)₆ and Mn₂(CO)₁₀], and the supported TiCl₄ on three commercial silicas having different surface areas: Davison 951, 952, and also the Dart 1000. It was found that the carriers affect the catalytic activity of the final catalyst and also its kinetic behavior. The supported Ziegler–Natta catalysts control more easily the nascent polymer particles (size, shape, and porosity) than the conventional ones. In addition the morphology of the catalysts and the subsequent polymer particles are closely related to the parent morphology of the silicas used as carriers. Furthermore, the nascent morphology of the polyethylenes obtained with the conventional TiCl₄–Et₂AlCl catalytic system can be modified by using different |Al|/|Ti| ratios, resulting in more dense, spherical, and bigger polymer particles by increasing this ratio. On the other hand, detailed studies on the texture or arrangement of the polymer particles reveal the existence of mainly two fine morphologies (globular and wormlike), which are the result of the order of the primary or elementary catalyst particles (microspheres and platelets), the force linking them together, and the activity of the polymerization centers placed on their surface.