Processing and performance of solid oxide fuel cell with Gd-doped ceria electrolyte

Fuel Cell performance was measured at 792-1095 K for Ni-GDC (Gd-doped ceria) anode-supported GDC film (60 μm thickness) with a (La_0.8Sr_0.2)(Co_0.8Fe_0.2)O₃ cathode using H₂ fuel containing 3 vol% H₂O. A maximum power density, 436 mW/cm², was obtained at 1095 K. The electrical conductivity of GDC electrolyte in N₂ atmosphere of 10⁻¹⁵-10⁰ Pa oxygen partial pressures (Po₂) at 773-1073 K was independent of Po₂, which indicated the diffusion of oxide ions. The conductivity of GDC in H₂O/H₂ atmosphere increased because of the further formation of electrons due to the dissociation of hydrogen in GDC (H₂ → 2H⁺ + 2e⁻). The hole conductivity was observed at 873 K in Po₂ = 10⁰-10⁴ Pa. The key factors in increasing power density are the increase of open circuit voltage and the suppression of H₂ fuel dissolution in GDC electrolyte. These are controlled by the cathode material and Gd-dopant composition.