Sequential Combination of Constituent Oxides in the Synthesis of Pb(Fe1/2Nb1/2)O3by Mechanical Activation

Pb(Fe_1/2Nb_1/2)O₃(PFN) has been successfully synthesized via a novel mechanical activation of mixed oxides and columbite precursor consisting of lead oxide and FeNbO₄. A nanocrystalline perovskite phase 5–15 nm in crystallite size was formed after 30 h of mechanical activation at room temperature for both types of starting materials. However, the nanocrystalline PFN phase derived from the mixed oxides of PbO, Fe₂O₃, and Nb₂O₅is unstable, and develops pyrochlore phases when calcined at 500°–900°C, while no pyrochlore phase is observed for the material derived from the columbite precursor consisting of PbO and FeNbO₅. Different sintering behavior and dielectric properties were also observed between the two types of PFN. These differences are accounted for by the compositional inhomogeneity in the material derived from the mixed oxides, as was revealed by Raman spectroscopic studies. This suggests that mechanical activation is analogous to thermal activation, where the phase development is strongly dependent on the sequence of combining the constituent oxides.