| Abstract: | Conjoint Action of Stress Corrosion Cracking and Fatigue on Corrosion Fatigue of a High Strength Steel The corrosion fatigue characteristics of a high strength, martensitic steel in 0.5 n NaCl solution is investigated with regard to the fatigue and stress corrosion cracking behaviour of the material. Test parameters are stress ratio and frequency, testing is carried out with fracture mechanics methods, the crack surfaces are examined fractographically. An analysis of the results reveals that corrosion fatigue in high strength steel is caused by fatigue or by stress corrosion cracking, depending on the kinetics of the two processes. Fatigue and stress corrosion cracking do not act cumulative or additive. Instead, the kinetically faster process causes crack advance. The crack growth characteristics are interpreted with respect to the fractographic appearance of the crack surfaces. Corrosion fatigue cracks propagate either intergranular relative to the prior austenite grain boundaries as stress corrosion cracks do or transgranular like fatigue cracks, depending on the crack growth rates of the two processes. Fatigue and stress corrosion cracking do not interact, at least in a measurable degree, because of the different crack path of the two fracture processes. Results can be assessed quantitatively with the “process competition model”. |