| Transient liquid phase diffusion bonding of a single crystal superalloy DD6 |
| |
| 作者单位： | Beijing Institute of Aeronautical Materials，Beijing，100095，Beijing Institute of Aeronautical Materials，Beijing，100095，Beijing Institute of Aeronautical Materials，Beijing，100095，Beijing Institute of Aeronautical Materials，Beijing，100095，Beijing Institute of Aeronautical Materials，Beijing，100095，Beijing Institute of Aeronautical Materials，Beijing，100095 |
| |
| 摘 要： | 0Introduction DD6isasecondgenerationsinglecrystalsuperalloy developedbyBeijingInstituteofAeronauticalMaterials, whichpossessesmanyadvantagessuchashighstrengthat elevatedtemperature,excellentcomprehensiveperform anceandgoodmicrostructuralstability.DD6allo…
|
Transient liquid phase diffusion bonding of a single crystal superalloy DD6 |
| |
| Authors: | Li Xiaohong Mao Wei GUO Wanlin Xie Yonghui Ye Lei Cheng Yaoyong |
| |
| Abstract: | DD6 alloy was bonded by transient liquid phase (TLP) diffusion bonding. The main compositions of the interlayer alloy employed were similar to those of the base metal, DD6, and a certain amount of element B was added as the melting point depressant. The results show that it is difficult to obtain the joints with the microstructures completely homogeneous. For the joint TLP diffusion bonded at 1 290℃ for 12 h, about half areas of the beam possessed a y + y' microstructure, nearly identical with that of the base metal, and the other local areas consisted of γ-solution, borides, etc. Prolonging the bonding time to 24 h, the inhomogeneous areas in the joint reduced, and the joint property improved. The joint stress-rupture strength at 980℃ and 1 100℃ reached90%-100% and 70%-80% of those of the base metal respectively. |
| |
| Keywords: | single crystal superalloy TLP diffusion bonding joint stress-rupture property |