| 渗碳淬火齿轮产生磨削裂纹原因分析及其预防措施 |
| |
| 引用本文： | 马轶群,任玉灿,肖溪. 渗碳淬火齿轮产生磨削裂纹原因分析及其预防措施[J]. 河北建筑工程学院学报, 2008, 26(3): 69-70 |
| |
| 作者姓名： | 马轶群 任玉灿 肖溪 |
| |
| 作者单位： | 河北建筑工程学院;河北建筑工程学院;河北建筑工程学院 |
| |
| 摘 要： | 通过对磨削裂纹形成原因的分析，得出磨削裂纹的产生主要是工件不良组织形态在磨削热的作用下，残余应力与热应力相互作用的结果，并归纳出防止产生齿轮磨削裂纹的措施．
|
| 关 键 词： | 磨削裂纹 原因分析 措施 |
The Reasons and Preventive Measures of the Grinding Cracks in Cementing and Hardening Gears |
| |
| Ma Yiqun,Ren Yucan,Xiao Xi. The Reasons and Preventive Measures of the Grinding Cracks in Cementing and Hardening Gears[J]. Journal of Hebei Institute of Architectural Engineering, 2008, 26(3): 69-70 |
| |
| Authors: | Ma Yiqun Ren Yucan Xiao Xi |
| |
| Affiliation: | (Hebei Institute of Architecture and Civil Engineering) |
| |
| Abstract: | Through analyzing the forming cause of the grinding cracks, the authors found the main forming cause of the grinding cracks is the mutual action of the reminder stress and heat stress, in which bad structure and morphology function under the grinding heat. |
| |
| Keywords: | grinding cracks analysis of the cause measures |