Structure and luminescence properties of Eu/Tb codoped oxyfluoride glass ceramics containing Sr2GdF7 nanocrystals

Eu/Tb codoped transparent oxyfluoride borosilicate glass ceramics containing Sr₂GdF₇ nanocrystals were fabricated under a reductive atmosphere and the conversion of Eu³⁺ ions to Eu²⁺ ions was observed. The Sr₂GdF₇ nanocrystals with an average size of 32 nm were homogeneously precipitated in the oxyfluoride borosilicate glass matrix, which could be evidenced by X-ray diffraction (XRD), transmission electron microscopy (TEM) and energy-dispersive X-ray (EDX) spectroscopy. The enhancement of photoluminescence emission intensity, reduction of the relative emission intensities between ⁵D₀ → ⁷F₂ and ⁵D₀ → ⁷F₁, and long fluorescence lifetimes of Eu²⁺, Eu³⁺, and Tb³⁺ ions revealed that more rare earth ions were partitioned into the low phonon energy environment Sr₂GdF₇ nanocrystals. Under ultraviolet excitation, pure and bright white light emission was obtained in the oxyfluoride borosilicate glass ceramic, which may be a potential blue, green and red-emitting phosphor for white LEDs.