 研究了铁素体区热轧高温卷取条件下，2种不同成分的IF钢的织构特征。结果表明，高温卷取后，普通Ti IF钢发生了完全再结晶，中心面和1/4面上形成了很强的<111>∥ND再结晶织构；高强Ti IF钢大部分晶粒仍处于轧制状态，只有极少部分晶粒发生了再结晶，中心面和1/4面上形成的织构组分以<110>∥RD为主，<111>∥ND再结晶织构较弱。织构分析表明，2种钢的表面织构均较弱，普通Ti IF钢表面上<001>∥ND组分占优，高强Ti IF钢表面上<110>∥ND组分强度最高。

Texture Characteristics of IF Steels After Ferritic Rolling and High Temperature Coiling

The texture characteristics of two different IF steels were studied after rolling in the ferritic range and coiling at high temperature. It was found that the ordinary Ti IF steel was recrystallized completely and strong <111>∥ND recrystallization texture was formed at the mid section and 1/4 section. However, in the high strength IF steel, most of the grains were still in as rolled condition after coiling and <110>∥RD texture was in the ascendant at the mid section and 1/4 section with very weak <111>∥ND recrystallization texture. Textures at surface in both steels were very weak and their <001>∥ND was dominant in ordinary Ti IF steel and <110>∥ND in high strength Ti IF steel was the strongest component.