Low-temperature H2-SCR of NO on a novel Pt/MgO-CeO2 catalyst

The selective catalytic reduction of NO by H₂ under strongly oxidizing conditions (H₂-SCR) in the low-temperature range of 100–200 °C has been studied over Pt supported on a series of metal oxides (e.g., La₂O₃, MgO, Y₂O₃, CaO, CeO₂, TiO₂, SiO₂ and MgO-CeO₂). The Pt/MgO and Pt/CeO₂ solids showed the best catalytic behavior with respect to N₂ yield and the widest temperature window of operation compared with the other single metal oxide-supported Pt solids. An optimum 50 wt% MgO-50wt% CeO₂ support composition and 0.3 wt% Pt loading (in the 0.1–2.0 wt% range) were found in terms of specific reaction rate of N₂ production (mols N₂/g_cat s). High NO conversions (70–95%) and N₂ selectivities (80–85%) were also obtained in the 100–200 °C range at a GHSV of 80,000 h⁻¹ with the lowest 0.1 wt% Pt loading and using a feed stream of 0.25 vol% NO, 1 vol% H₂, 5 vol% O₂ and He as balance gas. Addition of 5 vol% H₂O in the latter feed stream had a positive influence on the catalytic performance and practically no effect on the stability of the 0.1 wt% Pt/MgO-CeO₂ during 24 h on reaction stream. Moreover, the latter catalytic system exhibited a high stability in the presence of 25–40 ppm SO₂ in the feed stream following a given support pretreatment. N₂ selectivity values in the 80–85% range were obtained over the 0.1 wt% Pt/MgO-CeO₂ catalyst in the 100–200 °C range in the presence of water and SO₂ in the feed stream. The above-mentioned results led to the obtainment of patents for the commercial exploitation of Pt/MgO-CeO₂ catalyst towards a new NO_x control technology in the low-temperature range of 100–200 °C using H₂ as reducing agent. Temperature-programmed desorption (TPD) of NO, and transient titration of the adsorbed surface intermediate NO_x species with H₂ experiments, following reaction, have revealed important information towards the understanding of basic mechanistic issues of the present catalytic system (e.g., surface coverage, number and location of active NO_x intermediate species, NO_x spillover).