Tribological behaviour of plasma sprayed Al2O3 and TiO2 ceramic hard coatings under dry contact

Plasma sprayed ceramic coatings are used in a number of industries in which surface modification of components to compare tribological properties is important: so hence, are evaluations of their tribological properties. This paper presents a study on the wear behaviour of three ceramic coatings — Al₂O₃, TiO₂ and Al₂O₃-TiO₂combination — in the load and speed ranges of 5 to 50 N, and 0.3 to 10 m/s, respectively, on which few data are available in the literature. The tests were carried out using a standard dry sand rubber wheel abrasion test and a pin-on-disc machine under dry sliding conditions. It was found that a stick-slip effect seems to occur at low sliding speeds, and transition takes place at a sliding speed of around 4 m/s. Of the three ceramic coatings, TiO₂ was found to be the most wear resistant, with the least friction coefficient, although it is less hard than the Al₂O₃ coatings. Scanning electron microscopy of the surface shows evidence of wear mechanisms such as plastic deformation, transfer-film formation, micro cracks, and grain pull-out in the coatings.