Fracture behavior of glass bead-filled poly(oxymethylene) injection moldings
Authors:S Hashemi  K J Din  P Low
Abstract:The mechanical properties of glass bead filled poly(oxymethylene) were investigated as a function of glass bead content and glass bead diameter using injection molded test pieces. Fracture toughness measurements were made using single edge-notched tension and single edge-notched bend specimens. The effect of notch orientation with respect to the mold fill direction on fracture toughness was studied using single gate and double gate moldings. Tensile strength and flexural modulus were measured using standard test pieces. It was found that; (i) fracture toughness of the filled and unfilled polymer was relatively independent of notch orientation, (ii) the presence of weldlines in the molded test pieces did not affect the fracture toughness of unfilled polymer or its composites, (iii) fracture toughness of filled polymer was always considerably lower than that of the unfilled polymer; fracture toughness decreased sharply with increasing bead concentration, (iv) fracture toughness was not a sensitive function of glass bead diameter; it decreased slightly as bead diameter increased, (v) strain energy release rate as measured under impact decreased with increasing bead concentration, (vi) tensile strength decreased linearly with increasing glass bead concentration and was inversely proportional to the square root of the bead diameter, (vii) weldlines did not affect the tensile strength of the polymer or its composities, (viii) flexural modulus increased linearly with increasing glass bead concentration according to the Einstein equation.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号