| 石化厂湿硫化氢环境下钢的腐蚀开裂与选材 |
| |
| 引用本文： | 余存烨.石化厂湿硫化氢环境下钢的腐蚀开裂与选材[J].化工设备与管道,2009,46(6):60-66. |
| |
| 作者姓名： | 余存烨 |
| |
| 作者单位： | 中国石化上海石化股份有限公司,上海,200540 |
| |
| 摘 要： | 叙述了石化厂湿硫化氢环境下钢的腐蚀类型、应力腐蚀及氢致开裂的机理、影响因素、危害程度的评定以及防护对策。
|
| 关 键 词： | 湿硫化氢 硫化物应力腐蚀 氢致开裂 防护 选材 钢 石化设备 |
Corrosion Crack Occurred in Steel Used in Wet Hydrogen Sulfide Environment in Petrochemical Plant and Material Selection |
| |
| YU Cun-ye.Corrosion Crack Occurred in Steel Used in Wet Hydrogen Sulfide Environment in Petrochemical Plant and Material Selection[J].Process Equipment & Piping,2009,46(6):60-66. |
| |
| Authors: | YU Cun-ye |
| |
| Affiliation: | YU Cun-ye (SINOPEC Shanghai Petrochemical Co. , Ltd, Shanghai 200540, China) |
| |
| Abstract: | In this article, with respect to the hydrogen sulfide environment in petrochemical plant, the corrosion kind, the mechanism of stress corrosion and hydrogen induced cracking, the influence factors to stress corrosion, the assessment of harm and the corrosion protection measures were described. |
| |
| Keywords: | wet hydrogen sulfide sulfide induced stress corrosion hydrogen induced cracking protection |