| Synthesis of TiN/AlON composite ceramics |
| |
| 作者单位： | Xidong Wang，Lichun Gao，Guobao Li，and Wenchao LiDepartment of Physical Chemistry，University of Science and Technology Beijing，Beijing 100083，China |
| |
| 摘 要： | The synthesis process of TiN/AlON composite ceramics was studied, the thermodynamics, mechanical properties and micro-structures of TiN/AlON have also been investigated. The TiN/AlON composite ceramics has been synthesized by both hot-pressing and pressureless sintering. The characterizations of the material synthesized were analyzed with XRD (X-ray diffraction) and TEM (transmission electronic microscope). The density and toughness strength of TiN/AlON are 3.57g/cm3 and 4.74MPa.m1/2, respectively. The bending strength was measured at both room temperature and high temperatures and the results are 399 MPa (room temperature), 406 MPa (1 073 K), 417 MPa (1 273 K) and 323 MPa (1 573 K). Pattern Recognition (PR) and Artificial Neural Network (ANN) were used to optimize the parameters and to predict the expected values. A proper parameter for pressureless sintering of TiN/AlON has been obtained and testified, the parameters are temperature (1 978 K), AlN / (AlN + Al2O3) ratio (0.22), MgO (4.7%) and TiO2 (7.2
|
Synthesis of TiN/AlON composite ceramics |
| |
| Xidong Wang,Lichun Gao,Guobao Li,Wenchao Li. Synthesis of TiN/AlON composite ceramics[J]. Journal of University of Science and Technology Beijing, 2003, 10(1) |
| |
| Authors: | Xidong Wang Lichun Gao Guobao Li Wenchao Li |
| |
| Abstract: | The synthesis process of TiN/AlON composite ceramics was studied, the thermodynamics, mechanical properties and micro-structures of TiN/AlON have also been investigated. The TiN/AlON composite ceramics has been synthesized by both hot-pressing and pressureless sintering. The characterizations of the material synthesized were analyzed with XRD (X-ray diffraction) and TEM (transmission electronic microscope). The density and toughness strength of TiN/AlON are 3.57g/cm3 and 4.74MPa.m1/2, respectively. The bending strength was measured at both room temperature and high temperatures and the results are 399 MPa (room temperature), 406 MPa (1 073 K), 417 MPa (1 273 K) and 323 MPa (1 573 K). Pattern Recognition (PR) and Artificial Neural Network (ANN) were used to optimize the parameters and to predict the expected values. A proper parameter for pressureless sintering of TiN/AlON has been obtained and testified, the parameters are temperature (1 978 K), AlN / (AlN + Al2O3) ratio (0.22), MgO (4.7%) and TiO2 (7.2%). |
| |
| Keywords: | synthesis TiN AlON composite ceramics |