FRICTION PROPERTIES OF OIL-INFILTRATED POROUS AAO FILM ON AN ALUMINUM SUBSTRATE |
|
| Authors: | CX Jiang JP Tu SY Guo MF Fu XB Zhao |
| Affiliation: | 1. Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China;Department of Mechanical and Electronic Engineering, Nanchang University, Nanchang 330029, China 2. Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China 3. Department of Mechanical Engineering, Zhejiang Institute of Science and Technology, Hangzhou 310012,China 4. Department of Mechanical and Electronic Engineering, Nanchang University, Nanchang 330029, China |
| Abstract: | The porous anodic aluminum oxide (AAO) film on a pure aluminum substrate was prepared by a two-step anodization in a 0.3M oxalic acid solution and pore-enlargement treatment in the phosphoric acid aqueous solution at 50℃. The diameter of highly ordered pore on the AAO film was about 90nm, and the thickness of the AAO film was 3μm. The mineral oil was infiltrated in the ordered nanometer sized pores of AAO film on an aluminum substrate due to the capillarity effect. The friction coefficient was measured using a ball-on-disk tribotester.The tests were conducted at loads range from 490 to 2450mN and at sliding velocities beably improved the wear resistance. As compared to the porous AAO film, the oil-infiltrated specimen had low friction coefficient. With increasing the applied load and sliding velocity,the friction coefficient of the oil-infiltrated film decreased. It indicates that the oil-infiltrated AAO film produced a new way to modify the friction and wear of aluminum alloy. |
| Keywords: | friction coefficient oil-infiltrated AAO film aluminum substrate |
| 本文献已被 CNKI 万方数据 等数据库收录！ | |
| 点击此处可从《金属学报(英文版)》浏览原始摘要信息 | |
| 点击此处可从《金属学报(英文版)》下载全文 | |